Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % |
Melt Mass-Flow Rate | 230°C/2.16 kg | 内部方法 | 14 | g/10 min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO 527-2/1A/5 | 151 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 1.6 | % |
Tensile Modulus | | ISO 527-2/1A/1 | 14400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 111 | °C |
Glass Transition Temperature | | ISO 3146 | 110 | °C |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Permeability | 23°C 2 | DIN 53380-3 | 1.4 | cc-25µm/m²-day-atm |
Oxygen Permeability | 23°C 3 | DIN 53380-3 | 1.3 | cc-25µm/m²-day-atm |
Water Vapor Permeability | 38°C | DIN 53122 | 0.400 | g-25µm/(m² day-atm) |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 90 | °C |
Suggested Max Moisture | | | 0.010 | % |
Processing (Melt) Temp | | | 225 到 235 | °C |
Drying Time | | | 8.0 到 24 | hr |
Rear Temperature | | | 185 到 195 | °C |
Middle Temperature | | | 205 到 215 | °C |
Front Temperature | | | 205 到 215 | °C |
Nozzle Temperature | | | 200 到 210 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.