Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | normal | ISO 2577 | 0.0 | % |
Modeling Shrinkage | parallel | ISO 2577 | 0.50 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | 23℃ | ISO 180/1U | 35.0 | KJ/m |
Tensile Modulus | | ISO 527-1,-2/1 | 9800 | Mpa |
Tensile Strength | | ISO 527-1,-2/5 | 105 | Mpa |
Tensile Elongation | Break | ISO 527-1,-2/5 | 3.2 | % |
Flexural Modulus | 23℃ | ISO 178 | 10000 | Mpa |
Flexural Strength | 23℃ | ISO 178 | 125 | Mpa |
Notched Izod Impact Strength | 23℃ | ISO 180/1A | 5.20 | KJ/m |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | 50℃/h 50N | ISO 306 | 195 | °C |
Peak Crystallization Temperature | 10℃/min | ISO 11357-1,-3 | 335 | °C |
Deflection Temperature Under Load? | 1.80MPa | ISO 75-1,-2 | 230 | °C |
Coefficient of Linear Thermal Expansion | parallel | ISO 11359-1,-2 | 0.000011 | cm/cm℃ |
Coefficient of Linear Thermal Expansion | normal | ISO 11359-1,-2 | 0.000011 | cm/cm℃ |
Flammability | | UL 94 | V-0 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC 60243-1 | 46 | KV/mm |
Relative Permittivity | 1000Hz | IEC 60250 | 3.60 | |
Surface Resistivity | | IEC 60093 | 1E+15 | ohms |
Volume Resistivity | | IEC 60093 | 1E+14 | ohm.m |
Comparative Tracking Index | | IEC 60112 | 200 | |
Dissipation Factor? | 1000Hz | IEC 60250 | 0.031 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1740 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.