Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1.71 | g/cm³ |
Modeling Shrinkage | 流动 | ISO 294-4 | 0.1 | % |
Modeling Shrinkage | 垂直 | ISO 294-4 | 0.4 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23.0 °C | ISO 179/1eA | 27 | kJ/m² |
Charpy Unnotched Impact Strength | 23.0 °C | ISO 179/1eU | 16.6 | kJ/m² |
Unnotched Izod Impact Strength | 23.0 °C | ISO 180/1U | 28.0 | kJ/m² |
Tensile Modulus | | ISO 527-2/1A | 14000 | Mpa |
Tensile Strength | 断裂 | ISO 527-2/1A | 131 | Mpa |
Tensile Elongation | 断裂 | ISO 527-2/1A | 1.66 | % |
Flexural Modulus | | ISO 178 | 13100 | Mpa |
Flexural Strength | | ISO 178 | 198 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa | ISO 75-1, -2 | 285 | °C |
Melting temperature | 10°C/min | ISO 11357-1,-2,-3 | 318 | °C |
Coefficient of Linear Thermal Expansion | 流动 | ISO 11359-2 | 0.0000060 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | 垂直 | ISO 11359-2 | 0.000048 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 2.05 GHz | | 4.18 | |
Dissipation Factor? | 2.05 GHz | | 0.004 | |
Flame Rating | Test Condition | Test Method | Test Result | Unit |
---|
Fire rating | 1.50 mm | UL94 | V-0 | |
Fire rating | 0.800 mm | UL94 | V-0 | |
加工条件 | Test Condition | Test Method | Test Result | Unit |
---|
Mold Temperature | | cavity | 80.0 - 120 | °C |
下料段温度 | | | 40.0 - 60.0 | °C |
第一段温度 | | | 320 - 330 | °C |
第二段温度 | | | 335 - 345 | °C |
第三段温度 | | | 335 - 345 | °C |
第四段温度 | | | 335 - 345 | °C |
Nozzle Temperature | | | 335 - 345 | °C |
Processing (Melt) Temp | | | 325 - 345 | °C |
Drying Temperature | | | >= 150 | °C |
Drying Time | | | 3.00 | hour |
建议水分含量 | | | <= 0.010 | % |
注塑压力 | | | 50.0 - 150 | Mpa |
Holding Pressure | | | 50.0 - 150 | Mpa |
Back Pressure | | | <= 3.00 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.