LCP SUMIKASUPER® E4006 BK SUMITOMO JAPAN

Unit Price:
$6207 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:heat-resisting Low shrinkage Dimensional stability Low viscosity High temperature strength Weldable Aging resistance Antichemical
Application Areas:fibre
Color:--
Grade:Flame retardant grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	内部方法	0.78	%
Modeling Shrinkage	Modeling Shrinkage	流量	内部方法	0.11	%
Moisture Absorption	Saturation	ASTM D570	0.020	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength		ASTM D638	182	Mpa
Tensile Elongation	Break	ASTM D638	5.6	%
Flexural Modulus	23°C	ASTM D790	11900	Mpa
Flexural Modulus	Flexural Modulus	200°C	ASTM D790	5780	Mpa
Flexural Strength	23°C	ASTM D790	155	Mpa
Flexural Strength	Flexural Strength	200°C	ASTM D790	47.0	Mpa
Shearing Strength		ASTM D732	58.0	Mpa
Poisson Ratio		ASTM D785	0.48

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ASTM D648	310	°C
Thermal Conductivity		JIS R2618	0.53	W/m/K
Linear thermal expansion coefficient	Flow : 150°C	内部方法	2.0E-6	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 150°C	内部方法	8.1E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC 60112	185	V
Dissipation Factor?	1 kHz	ASTM D150	0.018
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.035
Dielectric Constant	1 kHz	ASTM D150	4.40
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.70
Arc Resistance		ASTM D495	130	sec
Volume Resistivity		ASTM D257	1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Time	4.0 到 24	hr
Rear Temperature	330 到 350	°C
Middle Temperature	350 到 370	°C
Front Temperature	370 到 390	°C
Nozzle Temperature	370 到 390	°C
Back Pressure	1.00 到 5.00	Mpa
Screw Speed	50 到 100	rpm
Injection Pressure	120 到 160	Mpa
Injection Rate	中等偏快
Drying Temperature	130	°C
Processing (Melt) Temp	380	°C
Mold Temperature	40 到 160	°C
Holding Pressure	40.0 到 60.0	Mpa

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	6.40 mm	ASTM D256	460	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	91

Flammability	Test Condition	Test Method	Test Result	Unit
Soldering Resistance		内部方法	335	°C
Oxygen Index		ISO 527-1,-2(JIS K7161,7162)	44	%
Flame Rating	0.30 mm, NC, BK	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.