LCP SUMIKASUPER® E6810LHF-BZ SUMITOMO JAPAN

Unit Price:
$7447 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
60MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow	ASTM D955	0.22	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow	ASTM D955	0.66	%
Moisture Absorption	Saturation	ASTM D570	0.020	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength		ASTM D638	126	Mpa
Tensile Elongation	Break	ASTM D638	4.3	%
Flexural Modulus	23°C	ASTM D790	13500	Mpa
Flexural Strength	23°C	ASTM D790	134	Mpa
Shearing Strength		ASTM D732	50.0	Mpa
Poisson Ratio		ASTM E132	0.39

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ASTM D648	284	°C
Linear thermal expansion coefficient	Flow : 50 to 150°C	ASTM D696	1.1E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 50 to 150°C	ASTM D696	6.5E-5	cm/cm/°C
RTI Elec	3.2 mm	UL 746	220	°C
RTI Imp	3.2 mm	UL 746	200	°C
RTI	3.2 mm	UL 746	240	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume Resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric Constant	1 kHz	ASTM D150	4.30
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.90
Dissipation Factor?	1 kHz	ASTM D150	0.019
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.028
Arc Resistance		ASTM D495	130	sec
Comparative Tracking Index		UL 746	165	V

Injection	Test Result	Unit
Drying Temperature	120 到 150	°C
Drying Time	3.0	hr
Suggested Max Regrind	30	%
Rear Temperature	300 到 320	°C
Middle Temperature	320 到 350	°C
Front Temperature	340 到 370	°C
Nozzle Temperature	340 到 370	°C
Mold Temperature	70 到 160	°C
Injection Pressure	78.0 到 157	Mpa
Injection Rate	中等偏快
Holding Pressure	20.0 到 39.0	Mpa
Back Pressure	0.980 到 4.90	Mpa
Screw Speed	50 到 100	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	6.40 mm	ASTM D256	280	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	103

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.30 mm	UL 94	V-0
Oxygen Index		ASTM D2863	46	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.