Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced Thermal stability Chemical resistance
Application Areas:Electrical field Electronic field Household appliances Household appliances
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.40	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.20	%
Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.040	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO 527-2/1A/5	190	Mpa
Tensile Strain	Break	ISO 527-2/1A/5	2.1	%
Tensile Creep Modulus	1 hr	ISO 899-1	12600	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1000 hr	ISO 899-1	10900	Mpa
Tensile Modulus		ISO 527-2/1A	15000	Mpa
Flexural Modulus	23°C	ISO 178	14500	Mpa
Flexural Stress	23°C	ISO 178	280	Mpa
Compressive Stress	1% Strain	ISO 604	100	Mpa
Compressive Modulus		ISO 604	14500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow	ISO 11359-2	6.0E-6	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow	ISO 11359-2	2.3E-5	cm/cm/°C
Melting Temperature		ISO 11357-3	280	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	250	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	235	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0 MPa, Unannealed	ISO 75-2/C	190	°C
Vicat Softening Temperature		ISO 306/B50	160	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100 Hz	IEC 60250	4.20
Relative Permittivity	Relative Permittivity	1 MHz	IEC 60250	3.70
Comparative Tracking Index		IEC 60112	175	V
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Arc Resistance		内部方法	140	sec
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm
Dissipation Factor?	100 Hz	IEC 60250	0.016
Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 60250	0.018
Dielectric Strength		IEC 60243-1	31	KV/mm

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.010	%
Processing (Melt) Temp	285 到 295	°C
Mold Temperature	80 到 120	°C
Drying Time	4.0 到 6.0	hr
Rear Temperature	270 到 280	°C
Middle Temperature	275 到 285	°C
Front Temperature	280 到 290	°C
Nozzle Temperature	290 到 300	°C
Back Pressure	< 3.00	Mpa
Hopper Temperature	20 到 30	°C
Injection Rate	快速

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	23°C	ISO 180/1U	29	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M -Sale	ISO 2039-2	85

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 4589-2	45	%
Flame Rating		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.