LCP VECTRA® A515D-2 BK CELANESE GERMANY

Unit Price:
$6207 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Good liquidity Hydrolysis resistance Halogen-free Flame retardant Mineral reinforcement
Application Areas:Thin walled products Electrical tools Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.60	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.0	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO 527-2/1A/5	175	Mpa
Tensile Strain	Break	ISO 527-2/1A/5	4.5	%
Tensile Modulus		ISO 527-2/1A	10500	Mpa
Flexural Modulus	23°C	ISO 178	11000	Mpa
Flexural Stress	23°C	ISO 178	175	Mpa
Compressive Stress	1% Strain	ISO 604	61.0	Mpa
Compressive Modulus		ISO 604	9500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ISO 306/A50, ISO 306/B50	149	°C
Melting Temperature		ISO 11357-3	280	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	232	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	185	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0 MPa, Unannealed	ISO 75-2/C	103	°C
Linear thermal expansion coefficient	Flow	ISO 11359-2	0.0	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow	ISO 11359-2	3.0E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	100 Hz	IEC 60250	0.010
Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 60250	0.020
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Arc Resistance		内部方法	145	sec
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric Strength		IEC 60243-1	40	KV/mm
Relative Permittivity	100 Hz	IEC 60250	3.80
Relative Permittivity	Relative Permittivity	1 MHz	IEC 60250	3.20
Comparative Tracking Index		IEC 60112	175	V

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.010	%
Processing (Melt) Temp	285 到 295	°C
Mold Temperature	80 到 120	°C
Drying Time	4.0 到 6.0	hr
Rear Temperature	270 到 280	°C
Middle Temperature	275 到 285	°C
Front Temperature	280 到 290	°C
Nozzle Temperature	290 到 300	°C
Back Pressure	< 3.00	Mpa
Hopper Temperature	20 到 30	°C
Injection Rate	快速

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	23°C	ISO 180/1U	130	kJ/m²
Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	100	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M -Sale	ISO 2039-2	63

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.