Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.40 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.20 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2/1A | 15000 | Mpa |
Tensile Stress | Break | ISO 527-2/1A/5 | 190 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 2.1 | % |
Tensile Creep Modulus | 1 hr | ISO 899-1 | 12600 | Mpa |
Tensile Creep Modulus | 1000 hr | ISO 899-1 | 10900 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 14500 | Mpa |
Flexural Stress | 23°C | ISO 178 | 280 | Mpa |
Compressive Modulus | | ISO 604 | 14500 | Mpa |
Compressive Stress | 1% Strain | ISO 604 | 100 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 250 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 235 | °C |
Deflection Temperature Under Load? | 8.0 MPa, Unannealed | ISO 75-2/C | 190 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 160 | °C |
Melting Temperature | | ISO 11357-3 | 280 | °C |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 6.0E-6 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 2.3E-5 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | > 1.0E+15 | ohms |
Volume Resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
Dielectric Strength | | IEC 60243-1 | 31 | KV/mm |
Relative Permittivity | 100 Hz | IEC 60250 | 4.20 | |
Relative Permittivity | 1 MHz | IEC 60250 | 3.70 | |
Dissipation Factor? | 100 Hz | IEC 60250 | 0.016 | |
Dissipation Factor? | 1 MHz | IEC 60250 | 0.018 | |
Arc Resistance | | 内部方法 | 140 | sec |
Comparative Tracking Index | | IEC 60112 | 175 | V |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 150 | °C |
Drying Time | | | 4.0 到 6.0 | hr |
Suggested Max Moisture | | | 0.010 | % |
Hopper Temperature | | | 20 到 30 | °C |
Rear Temperature | | | 270 到 280 | °C |
Middle Temperature | | | 275 到 285 | °C |
Front Temperature | | | 280 到 290 | °C |
Nozzle Temperature | | | 290 到 300 | °C |
Processing (Melt) Temp | | | 285 到 295 | °C |
Mold Temperature | | | 80 到 120 | °C |
Injection Rate | | | 快速 | |
Back Pressure | | | < 3.00 | Mpa |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO 180/1U | 29 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M -Sale | ISO 2039-2 | 85 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | | UL 94 | V-0 | |
Oxygen Index | | ISO 4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.