Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow | ASTM D955 | 0.22 | % |
Modeling Shrinkage | Across Flow | ASTM D955 | 0.66 | % |
Moisture Absorption | Saturation | ASTM D570 | 0.020 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ASTM D638 | 126 | Mpa |
Tensile Elongation | Break | ASTM D638 | 4.3 | % |
Flexural Modulus | 23°C | ASTM D790 | 13500 | Mpa |
Flexural Strength | 23°C | ASTM D790 | 134 | Mpa |
Shearing Strength | | ASTM D732 | 50.0 | Mpa |
Poisson Ratio | | ASTM E132 | 0.39 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648 | 284 | °C |
Linear thermal expansion coefficient | Flow : 50 to 150°C | ASTM D696 | 1.1E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow : 50 to 150°C | ASTM D696 | 6.5E-5 | cm/cm/°C |
RTI Elec | 3.2 mm | UL 746 | 220 | °C |
RTI Imp | 3.2 mm | UL 746 | 200 | °C |
RTI | 3.2 mm | UL 746 | 240 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
Dielectric Constant | 1 kHz | ASTM D150 | 4.30 | |
Dielectric Constant | 1 MHz | ASTM D150 | 3.90 | |
Dissipation Factor? | 1 kHz | ASTM D150 | 0.019 | |
Dissipation Factor? | 1 MHz | ASTM D150 | 0.028 | |
Arc Resistance | | ASTM D495 | 130 | sec |
Comparative Tracking Index | | UL 746 | 165 | V |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 120 到 150 | °C |
Drying Time | | | 3.0 | hr |
Suggested Max Regrind | | | 30 | % |
Rear Temperature | | | 300 到 320 | °C |
Middle Temperature | | | 320 到 350 | °C |
Front Temperature | | | 340 到 370 | °C |
Nozzle Temperature | | | 340 到 370 | °C |
Mold Temperature | | | 70 到 160 | °C |
Injection Pressure | | | 78.0 到 157 | Mpa |
Injection Rate | | | 中等偏快 | |
Holding Pressure | | | 20.0 到 39.0 | Mpa |
Back Pressure | | | 0.980 到 4.90 | Mpa |
Screw Speed | | | 50 到 100 | rpm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | 6.40 mm | ASTM D256 | 280 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTM D785 | 103 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.30 mm | UL 94 | V-0 | |
Oxygen Index | | ASTM D2863 | 46 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.