Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.82 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.01 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTM D955 | 0.20 | % |
Modeling Shrinkage | TD | ASTM D955 | 0.29 | % |
Moisture Absorption | 24 hr | ASTM D570 | 0.010 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ASTM D638/ISO 527 | 135 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 2.5 | % |
Tensile Elongation | Break | ASTM D1708 | 2.5 | % |
Rockwell Hardness | R -Sale | ASTM D785 | 105 | |
Flexural Modulus | | ASTM D790 | 17000 | Mpa |
Flexural Modulus | | ASTM D790/ISO 178 | 17 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 170 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790 | 170 | Mpa |
Unnotched Izod Impact Strength | | ASTM D256 | 60 | J/m |
Tensile Strength | | ASTM D638 | 135 | Mpa |
Izod notch impact strength | | ASTM D256/ISO 179 | 60 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.380 mm | UL 94 | V-0 | |
Coefficient of Linear Thermal Expansion | Flow | ASTM D696 | 0.000013 | cm/cm/℃ |
Coefficient of Linear Thermal Expansion | Across Flow | ASTM D696 | 0.000015 | cm/cm/℃ |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648 | 265 | °C |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 265 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 1.3/1.5 | mm/mm.℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | ASTM D149 | 50 | KV/mm |
Dielectric Constant | | ASTM D150 | 4.50 | |
Arc Resistance | | ASTM D495 | 190 | sec |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.