LCP LAPEROS® C130 JAPAN POLYPLASTIC

107

Unit Price:
$6206 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant High temperature resistan Glass fiber reinforced High mobility
Application Areas:Electrical field Electronic field Household appliances Household appliances
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.40	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.20	%
Density		ISO 1183	1.62	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	23°C	ISO 178	245	Mpa
Compressive Stress	1% Strain	ISO 604	139	Mpa
Compressive Modulus		ISO 604	22000	Mpa
Tensile Creep Modulus	1 hr	ISO 899-1	13600	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1000 hr	ISO 899-1	11700	Mpa
Tensile Stress	Break	ISO 527-2/1A/5	160	Mpa
Tensile Strain	Break	ISO 527-2/1A/5	1.9	%
Tensile Modulus		ISO 527-2/1A	15000	Mpa
Flexural Modulus	23°C	ISO 178	14000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	250	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	255	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0 MPa, Unannealed	ISO 75-2/C	211	°C
Linear thermal expansion coefficient	Flow	ISO 11359-2	6.0E-6	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow	ISO 11359-2	1.8E-5	cm/cm/°C
Melting Temperature		ISO 11357-3	325	°C
Vicat Softening Temperature		ISO 306/B50	192	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC 60243-1	35	KV/mm
Relative Permittivity	100 Hz	IEC 60250	4.20
Relative Permittivity	Relative Permittivity	1 MHz	IEC 60250	3.70
Comparative Tracking Index		IEC 60112	200	V
Dissipation Factor?	100 Hz	IEC 60250	0.014
Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 60250	0.018
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Arc Resistance		内部方法	182	sec
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	150	°C
Suggested Max Moisture	0.010	%
Processing (Melt) Temp	320 到 340	°C
Mold Temperature	80 到 120	°C
Drying Time	4.0 到 6.0	hr
Rear Temperature	290 到 300	°C
Middle Temperature	300 到 310	°C
Front Temperature	310 到 320	°C
Nozzle Temperature	310 到 330	°C
Back Pressure	< 3.00	Mpa
Hopper Temperature	20 到 30	°C
Injection Rate	快速

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	28	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25	kJ/m²
Notched Izod Impact Strength	23°C	ISO 180/1A	20	kJ/m²
Notched Izod impact strength	23°C	ISO 180/1U	26	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M -Sale	ISO 2039-2	80

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating		UL 94	V-0
Oxygen Index		ISO 4589-2	45	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.