Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.61 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.02 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23℃蘸涂,Equilibrium状态 | ASTM D-570 | 0.05 | % |
Moisture Absorption | 23℃ 50%相对温度Equilibrium状态 | ASTM D-570 | 0.05 | % |
Poisson Ratio | | | 0.49 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | | ASTM D-256 | 2300 | Mpa |
Shearing Strength | | ASTM D-732 | 84 | Mpa |
Notched Izod Impact Strength | 带Notched | ASTM D-256 | 137 | J/m |
Tensile Modulus | 3.2mmt | ASTM D-638 | 17600 | Mpa |
Tensile Strength | 3.2mmt | ASTM D-638 | 210 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 210 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | 3.2mmt | ASTM D-638 | 2.2 | % |
Rockwell Hardness | | ASTM D-785 | 84 | R |
Flexural Modulus | 3.2mmt | ASTM D-790 | 14700 | Mpa |
Flexural Modulus | | ASTM D790/ISO 178 | 15000 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 270 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | 3.2mmt | ASTM D-790 | 253 | Mpa |
Charpy impact strength | | ASTM D256/ISO 179 | 35 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V-0 | |
Deflection Temperature Under Load? | 1.82MPa | ASTM D-648 | 230 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | | ASTM D150/IEC 60250 | 4.1 | |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.7 | |
Arc Resistance | | ASTM D495/IEC 60112 | 137 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 3 x 10^16 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.