Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.50到0.70 | % |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50到0.70 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.30 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.60 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield3 | ASTMD638 | 58.0 | Mpa |
Tensile Strength | Yield | ISO527-2/50 | 58.0 | Mpa |
Tensile Strength | Break3 | ASTMD638 | 50.0 | Mpa |
Tensile Strength | Break | ISO527-2/50 | 55.0 | Mpa |
Tensile Modulus | --2 | ASTMD638 | 2250 | Mpa |
Tensile Modulus | -- | ISO527-2/1 | 2250 | Mpa |
Tensile Elongation | Yield3 | ASTMD638 | 5.3 | % |
Tensile Elongation | Yield | ISO527-2/50 | 5.2 | % |
Tensile Elongation | Break3 | ASTMD638 | 75 | % |
Tensile Elongation | Break | ISO527-2/50 | 75 | % |
Flexural Modulus | 50.0mmSpan4 | ASTMD790 | 2300 | Mpa |
Flexural Modulus | --5 | ISO178 | 2300 | Mpa |
Flexural Stress | --5,6 | ISO178 | 85.0 | Mpa |
Flexural Stress | Yield,50.0mmSpan4 | ASTMD790 | 87.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ball PressureTest | 75°C | IEC60695-10-2 | 通过 | |
Ball PressureTest | 100°C10 | IEC60695-10-2 | 通过 | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 128 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 110 | °C |
Vicat Softening Temperature | -- | ASTMD15259 | 131 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 133 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831 | 8E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | >1.0E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 90.0 | J |
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 90.0 | J |
Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 | |
Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 | |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 25 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 50 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.