Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ISO294-4 | 0.60 | % |
Melt Mass-Flow Rate | 260°C/5.0kg | ISO1133 | 14 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | >50 | % |
Tensile Stress | Yield | ISO527-2 | 49.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 4.0 | % |
Tensile Modulus | | ISO527-2 | 2250 | Mpa |
Flexural Modulus | | ISO178 | 2200 | Mpa |
Flexural Stress | | ISO178 | 77.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 100 | °C |
Vicat Softening Temperature | | ISO306/B50 | 122 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1.00GHz | IEC60250 | 6E-03 | |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Relative | 1.00GHz | IEC60250 | 3.00 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
Multi-Axial Instrumented Impact Energy | -20°C2 | 内部方法 | 20.0 | J |
Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 35.0 | J |
Multi-Axial Instrumented Impact Energy | 23°C2 | 内部方法 | 25.0 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.