Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow : 3.20 mm | ASTM D955 | 0.40 到 0.70 | % |
Modeling Shrinkage | Across Flow : 3.20 mm | ASTM D955 | 0.40 到 0.70 | % |
Modeling Shrinkage | Across Flow : 2.00 mm | ISO 294-4 | 0.40 到 0.70 | % |
Modeling Shrinkage | 流量 : 2.00 mm | ISO 294-4 | 0.40 到 0.70 | % |
Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238, ISO 1133 | 33 | g/10 min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break 3 | ASTM D638 | 50 | % |
Tensile Elongation | Break | ISO 527-2/50 | 60 | % |
Flexural Modulus | -- 4 | ASTM D790 | 2500 | Mpa |
Flexural Modulus | -- 5 | ISO 178 | 2650 | Mpa |
Flexural Strength | -- 4 | ASTM D790 | 90.0 | Mpa |
Flexural Strength | -- 5 | ISO 178 | 90.0 | Mpa |
Tensile Strength | Yield 3 | ASTM D638 | 62.0 | Mpa |
Tensile Strength | Yield | ISO 527-2/50 | 60.0 | Mpa |
Tensile Strength | Break 3 | ASTM D638 | 59.0 | Mpa |
Tensile Strength | Break | ISO 527-2/50 | 50.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO 306/B50 | 100 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 88.0 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 82.0 | °C |
RTI | 1.5 to 3.0 mm | UL 746 | 90.0 | °C |
RTI Imp | 1.5 to 3.0 mm | UL 746 | 85.0 | °C |
RTI Elec | 1.5 to 3.0 mm | UL 746 | 90.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
High Amp Arc Ignition | 1.5 mm | UL 746 | PLC 3 | |
Comparative Tracking Index | | IEC 60112 | PLC 0 | |
Hot-wire Ignition | 1.5 mm | UL 746 | PLC 2 | |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Injection Pressure | | | 98.1 | Mpa |
Desiccant Dryer | | | 2.0 到 4.0 | hr |
Desiccant Dryer | | | 80 | °C |
vacuum dryer | | | 80 | °C |
vacuum dryer | | | > 4.0 | hr |
Suggested Max Moisture | | | < 0.050 | % |
Mold Temperature | | | 50 到 70 | °C |
Rear Temperature | | | 230 到 250 | °C |
Middle Temperature | | | 240 到 260 | °C |
Front Temperature | | | 250 到 270 | °C |
Nozzle Temperature | | | 270 | °C |
Back Pressure | | | 0.490 到 1.96 | Mpa |
Screw Speed | | | 50 到 150 | rpm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTM D785 | 118 | |
Rockwell Hardness | R -Sale | ISO 2039-2 | 118 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.2 mm | UL 94 | V-1 | |
Flame Rating | 1.5 to 3.0 mm | UL 94 | V-0 | |
Flame Rating | 2.0 to 3.0 mm | UL 94 | 5VB | |
Flame Rating | 3.0 mm | UL 94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.