PC/ABS CYCOLOY™ CX7240-7T1D193 SABIC INNOVATIVE SHANGHAI

Unit Price:
$3969 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
11MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Middle flow Chemical resistance Rapid prototyping
Application Areas:Office equipment Thin walled products Electronic and electrical Communication equipment
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.40to0.60	%
Moisture Absorption	Saturation,23°C	ISO62	0.20	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.10	%
Melt Mass-Flow Rate	260°C/2.16kg	ASTMD1238	18	g/10min
Melt Volume flow Rate	260°C/2.16kg	ISO1133	15.0	cm3/10min
Density / Specific Gravity		ASTMD792	1.19	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.20	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTMD638	100	%
Flexural Modulus		ISO178	2500	Mpa
Flexural Strength		ISO178	96.0	Mpa
Tensile Modulus		ISO527-2/1	2600	Mpa
Tensile Elongation	Yield	ASTMD638	4.1	%
Tensile Modulus		ASTMD638	2600	Mpa
Tensile Strength	Yield	ASTMD638	65.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	58.0	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	2500	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	104	Mpa
Tensile Stress	Yield	ISO527-2/50	65.0	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/50	50.0	Mpa
Tensile Strain	Yield	ISO527-2/50	4.0	%
Tensile Strain	Tensile Strain	Break	ISO527-2/50	90	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTIElec		UL746	90.0	°C
Evolution Calendar intelligent importer		UL746	90.0	°C
RTIStr		UL746	90.0	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to40°C	ISO11359-2	7.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ISO11359-2	7.5E-05	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	100	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	89.0	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,6.40mm	ASTMD648	99.0	°C
Vicat Softening Temperature		ASTMD152512	110	°C
	Vicat Softening Temperature	--	ISO306/B50	110	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	113	°C
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	93.0	°C
Thermal Conductivity		ISO8302	0.20	W/m/K
Ball PressureTest	75°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot-wire Ignition	HWI	UL746	PLC3
High Amp Arc Ignition	HAI	UL746	PLC0
Comparative Tracking Index	CTI	UL746	PLC3
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric Strength	0.800mm,in Oil	IEC60243-1	35	KV/mm
	Dielectric Strength	1.60mm,in Oil	IEC60243-1	25	KV/mm
	Dielectric Strength	Dielectric Strength	3.20mm,in Oil	IEC60243-1	17	KV/mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	65.0	J
Charpy Notched Impact Strength	-30°C7	ISO179/1eA	10	kJ/m²
	Charpy Notched Impact Strength	23°C8	ISO179/1eA	22	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C7	ISO179/1eA	20	kJ/m²
Notched Izod Impact Strength	-30°C	ASTMD256	180	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	700	J/m
		Notched Izod Impact Strength	-30°C9	ISO180/1A	10	kJ/m²
			Notched Izod Impact Strength	-30°C10	ISO180/1A	10	kJ/m²
				Notched Izod Impact Strength	23°C9	ISO180/1A	25	kJ/m²
				Notched Izod Impact Strength	Notched Izod Impact Strength	23°C10	ISO180/1A	20	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.60mm	UL94	V-1
	UL flame retardant rating	0.75mm	UL94	V-0
		UL flame retardant rating	1.5mm	UL94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Glow Wire Flammability Index	0.75mm13	IEC60695-2-12	960	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	0.75mm	IEC60695-2-12	960	°C
Oxygen Index		ISO4589-2	35	%
Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	800	°C
	Glow Wire Ignition Temperature	0.75mm13	IEC60695-2-13	775	°C
		Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	825	°C
			Glow Wire Ignition Temperature	1.5mm13	IEC60695-2-13	775	°C
			Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm13	IEC60695-2-13	775	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.