PC/ABS INFINO® HM-1100 K21294 Samsung Cheil South Korea
39
- Unit Price:
- $4020 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 24MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.10 | % |
| TD | ASTMD955 | 0.10 | % | |
| TD | ISO2577 | 0.10 | % | |
| MD:3.20mm | ISO2577 | 0.10 | % | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 22 | g/10min |
| 250°C/2.16kg | ASTMD1238 | 7.0 | g/10min | |
| 220°C/10.0kg | ISO1133 | 22 | g/10min | |
| 250°C/2.16kg | ISO1133 | 7.0 | g/10min | |
| Ash Content | -- | ISO3451 | 9.5 | % |
| -- | ASTMD5630 | 9.5 | % | |
| Tg(halfwidth)-DSC | 101 | °C |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Break | ASTMD638 | 59.0 | Mpa |
| Yield | ASTMD638 | 59.0 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 4.0 | % |
| Flexural Strength | ASTMD790 | 96.0 | Mpa | |
| Flexural Stress | ISO178 | 95.0 | Mpa | |
| Tensile Modulus | ASTMD638 | 3400 | Mpa | |
| Flexural Modulus | ISO178 | 3800 | Mpa | |
| Flexural Modulus | ASTMD790 | 3900 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 55.0 | Mpa |
| Break | ISO527-2/5 | 55.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/5 | 4.0 | % |
| Tensile Modulus | ISO527-2/5 | 3400 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 97.0 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 97.0 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 102 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 96.0 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 96.0 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 98.0 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 99.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 | kJ/m² |
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 7.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 118 | |
| R-Scale | ISO2039-2 | 118 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.