PC/ABS CYCOLOY™ CX7240U-8D8T159 SABIC INNOVATIVE NANSHA

Unit Price:
$4682 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
22.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High impact resistance
Application Areas:Electrical applications Automotive interior parts
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.20	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%
Melt Mass-Flow Rate	260°C/2.16 kg	ASTM D1238	16	g/10 min
Melt Volume flow Rate	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.60	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	2950	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2530	Mpa
Tensile Elongation	Yield 3	ASTM D638	4.1	%
	Tensile Elongation	Yield	ISO 527-2/50	4.0	%
		Tensile Elongation	Break 3	ASTM D638	100	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	90	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2750	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2500	Mpa
Tensile Strength	Yield 3	ASTM D638	65.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	65.0	Mpa
		Tensile Strength	Break 3	ASTM D638	58.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	50.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	96.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	104	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI Elec		UL 746	90.0	°C
Vicat Softening Temperature	--	ASTM D152510	106	°C
	Vicat Softening Temperature	--	ISO 306/B50	110	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	113	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.3E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	6.2E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	5.4E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	5.4E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	93.0	°C
Ball PressureTest	73 to 77°C	IEC 60695-10-2	通过

Electrical performance	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 3
Hot-wire Ignition	UL 746	PLC 3
High Amp Arc Ignition	UL 746	PLC 0

Injection	Test Result	Unit
Hopper Temperature	60 到 80	°C
Drying Time	4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	260 到 300	°C
Middle Temperature	260 到 300	°C
Front Temperature	265 到 300	°C
Nozzle Temperature	265 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.038 到 0.076	mm
Drying Temperature	90	°C
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	270 到 300	°C
Mold Temperature	60 到 90	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	65.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	825	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	800	°C
Flame Rating	0.40 mm	UL 94	V-2
	Flame Rating	0.60 mm	UL 94	V-1
		Flame Rating	0.75 mm	UL 94	V-0
			Flame Rating	1.5 mm	UL 94	5VB
			Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.