PC/ABS Bayblend® FR3013 901510 COVESTRO GERMANY

Unit Price:
$3095 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
37MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Volume flow Rate	240°C/5.0 kg	ISO 1133	26.0	cm3/10min
Modeling Shrinkage (Across Flow)	2.00 mm 3	ISO 294-4	0.40 到 0.60	%
Modeling Shrinkage (Across Flow)	Modeling Shrinkage (Across Flow)	3.00 mm 4	ISO 2577	0.40 到 0.60	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	23°C	ISO 527-2/1	2650	Mpa
Tensile Stress	Yield, 23°C	ISO 527-2/50	61.0	Mpa
Tensile Stress	Tensile Stress	Break, 23°C	ISO 527-2/50	44.0	Mpa
Tensile Strain	Yield, 23°C	ISO 527-2/50	4.0	%
Tensile Strain	Tensile Strain	Break, 23°C	ISO 527-2/50	30	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	7.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	7.6E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	86.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	78.0	°C
Vicat Softening Temperature	--	ISO 306/B50	89.0	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	95.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC 60093	5.0E+17	ohms
Volume Resistivity	23°C	IEC 60093	2.0E+18	ohms·cm

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	240°C	ISO 11443-A	155	Pa·s
ISO Shortname			PC+ABS-FR(40)

Injection	Test Result	Unit
Drying Temperature ()	80	°C
Dry Air Dryer	4.0	hr
Suggested Max Moisture	< 0.020	%
Processing (Melt) Temp	240 到 270	°C
Mold Temperature	60 到 90	°C
Suggested Shot Size	30 到 70	%
Rear Temperature	220 到 230	°C
Middle Temperature	225 到 235	°C
Front Temperature	230 到 240	°C
Nozzle Temperature	255 到 265	°C
Back Pressure	5.00 到 15.0	Mpa
Vent Depth	0.025 到 0.075	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	23°C	ISO 180	无断裂

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 4589-2	31	%
Flame Rating	1.5 mm	UL 94	V-0 5VB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.