PC/ABS MULTILON® DN-7730M JIAXING TEIJIN
87
- Unit Price:
- $3528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High rigidity Bromine free Filler: Mineral filler Fillers mineral fillers Filler 30% filler by we
- Application Areas:Industrial applications Business equipment Industrial applications Business equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.20to0.40 | % |
| MD:4.00mm | 内部方法 | 0.10to0.30 | % | |
| TD：4.00mm | 内部方法 | 0.2到0.4 | % | |
| MD：4.00mm | 内部方法 | 0.1到0.3 | % | |
| Density | ISO 1183 | 1.4 | g/m3 | |
| ISO1183 | 1.40 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 3 | kJ/m² | |
| Flexural Stress | ISO178 | 100 | Mpa | |
| ISO 178 | 100 | Mpa | ||
| Charpy Unnotched Impact Strength | ISO 179 | 18 | kJ/m² | |
| Tensile Stress | 断裂 | ISO 527-2/5 | 66 | Mpa |
| 断裂 | ISO527-2/5 | 66.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/5 | 2.0 | % |
| 断裂 | ISO 527-2/5 | 2.0 | % | |
| Tensile Modulus | ISO527-2/1 | 9000 | Mpa | |
| ISO 527-2/1 | 9000 | Mpa | ||
| Flexural Modulus | ISO178 | 8000 | Mpa | |
| ISO 178 | 8000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO 75-2/B | 120 | ℃ |
| 热变形温度，1.80MPa,未退火 | ISO 75-2/A | 108 | ℃ | |
| 维卡软化温度 | ISO 306/B50 | 122 | ℃ | |
| 线形热膨胀系数，流动 | ISO 11359-2 | 3E-05 | cm/cm/℃ | |
| 线形热膨胀系数，横向 | ISO 11359-2 | 3.5E-05 | cm/cm/℃ | |
| 0.45MPa,未退火 | ISO75-2/B | 120 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 108 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 122 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 3.2E-05 | cm/cm/°C |
| TD | ISO11359-2 | 3.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 | ohms |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | 18 | kJ/m² | |
| Charpy Notched Impact Strength | ISO179 | 3.0 | kJ/m² |
| Deflection Temperature Under Load? | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical performance | 表面电阻率 | IEC 60093 | 1E+16 | ohms |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.