Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.20mm | | 0.25到0.45 | % |
Modeling Shrinkage | MD:3.20mm | | 0.25到0.45 | % |
Modeling Shrinkage | 吸水率(Saturation,23°C) | | 0.20 | % |
Melt Mass-Flow Rate | 260°C/2.16kg | ISO1133 | 25 | g/10min |
Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 23.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2 | 2800 | Mpa |
Flexural Modulus | | ISO178 | 2600 | Mpa |
Flexural Stress | | ISO178 | 88.0 | Mpa |
Nominal Tensile Strain at Break | | ISO527-2 | 44 | % |
Tensile Stress | Yield | ISO527-2 | 55.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 3.5 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
0.45MPa, Unannealed | | ISO75-2/B | 86.0 | °C |
1.8MPa, Unannealed | | ISO75-2/A | 77.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 无断裂 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.00mm | UL94 | V-1 | |
UL flame retardant rating | 1.50mm | UL94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.