Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40to0.70 | % |
Melt Mass-Flow Rate | 260°C/5.0kg | ISO1133 | 14 | g/10min |
Apparent Density | | ISO60 | 0.67 | g/cm³ |
Voc Content | | VDA277 | 9.00 | µg/g |
Spiral Flow | | | 45.0 | CM |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominalstrainatbreak | | ISO527-22 | >50 | % |
Flexural Modulus | | ISO178 | 2200 | Mpa |
Tensile Stress | Yield | ISO527-2/5 | 58.0 | Mpa |
Tensile Stress | Yield | ISO527-22 | 57.0 | Mpa |
Tensile Strain | Yield | ISO527-22 | 4.8 | % |
Tensile Strain | Break | ISO527-2/5 | >80 | % |
Tensile Modulus | | ISO527-2/1 | 2350 | Mpa |
Tensile Modulus | | ISO527-22 | 2350 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa | ISO75-22 | 130 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 110 | °C |
Deflection Temperature Under Load? | 1.8MPa | ISO75-22 | 110 | °C |
Vicat Softening Temperature | | ISO306/B50 | 132 | °C |
Vicat Softening Temperature | 50N | ISO3062 | 132 | °C |
Linear thermal expansion coefficient | MD:-30to80°C | ISO11359-2 | 7.1E-05 | cm/cm/°C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
CharpyNotchedImpactStrength | 23°C | ISO179/1eA2 | 35.0 | kJ/m² |
Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
Charpy Notched Impact Strength | -30°C | ISO179/1eU2 | NoBreak | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
BurningBehav.at1.6mmnom.thickn. | 1.60mm,UL | 4.21 | HB | |
Oxygenindex | | ISO4589-22 | 21 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.