Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 13 | g/10min |
Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 12.6 | cm3/10min |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30到0.50 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.30到0.50 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.26 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.060 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Yield | | ASTMD638 | 54.0 | Mpa |
Break | | ASTMD638 | 44.0 | Mpa |
yield | | ISO527-2/5 | 3.6 | % |
yield | | ISO527-2/5 | 58.0 | Mpa |
fracture | | ISO527-2/5 | 38.0 | Mpa |
fracture | | ISO527-2/5 | 78 | % |
50.0mm Span | | ASTMD790 | 3180 | Mpa |
--7 | | ISO178 | 3270 | Mpa |
--8 | | ISO178 | 95.0 | Mpa |
--1 | | ASTMD638 | 3310 | Mpa |
Yield | | ASTMD638 | 3.5 | % |
Break | | ASTMD638 | 74 | % |
Yield,50.0mm Span | | ASTMD790 | 96.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 80.0 | °C |
1.8MPa, Unannealed,6.40mm | | ASTMD648 | 87.0 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 83.0 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831,ISO11359-2 | 6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831,ISO11359-2 | 6E-05 | cm/cm/°C |
-- | | ISO 1183 | 103 | °C |
-- | | ISO306/B120 | 106 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 11 | kJ/m² |
-30°C | | ASTMD256 | 71 | J/m |
-30°C11 | | ISO180/1A | 7.0 | kJ/m² |
23°C12 | | ISO180/1A | 31 | kJ/m² |
23°C | | ASTMD256 | 320 | J/m |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.800mm | UL94 | V-0 | |
UL flame retardant rating | 0.00mm | UL94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.