Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO2577 | 0.20to0.40 | % |
Modeling Shrinkage | MD | ISO2577 | 0.20to0.40 | % |
Melt Volume flow Rate | 240°C/5.0kg | ISO1133 | 9.00 | cm3/10min |
Melt Viscosity | 260°C | ISO11443-A | 211 | Pa·s |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/50 | 41.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2/50 | 2.9 | % |
Tensile Strain | Break,23°C | ISO527-2/50 | 4.0 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 4600 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 92.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 84.0 | °C |
Vicat Softening Temperature | | ISO306/B120 | 97.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180 | 70 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.