PC/ABS INFINO® WP-1041G Samsung Cheil South Korea
98
- Unit Price:
- $3701 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant
- Application Areas:TV Monitor
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| TD：3.20mm | ASTMD955 | 0.40to0.70 | % | |
| TD:3.20mm | ISO2577 | 0.40to0.70 | % | |
| MD:3.20mm | ISO2577 | 0.40to0.70 | % | |
| Melt Mass-Flow Rate | 250°C/10.0kg | ASTMD1238 | 31 | g/10min |
| 250°C/2.16kg | ASTMD1238 | 3.0 | g/10min | |
| 250°C/10.0kg | ISO1133 | 31 | g/10min | |
| 250°C/2.16kg | ISO1133 | 3.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ASTMD790 | 1900 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 39.0 | Mpa |
| Yield | ASTMD638 | 49.0 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 100 | % |
| Flexural Strength | ASTMD790 | 66.0 | Mpa | |
| Flexural Stress | ISO178 | 70.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 47.0 | Mpa |
| Break | ISO527-2/50 | 41.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | 73 | % |
| Tensile Modulus | ISO527-2/50 | 1900 | Mpa | |
| Tensile Modulus | ASTMD638 | 1900 | Mpa | |
| Flexural Modulus | ISO178 | 2000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 120 | °C |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 116 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 100 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 101 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 111to113 | °C |
| -- | ISO306/B120 | 114 | °C | |
| Linear thermal expansion coefficient | MD：40to100°C | ASTME831 | 8.5E-05 | cm/cm/°C |
| MD：40to100°C | ISO11359-2 | 8.5E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 35 | kJ/m² |
| 23°C | ISO180/1A | 45 | kJ/m² | |
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 47 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 105 | |
| R-Scale | ISO2039-2 | 107 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.