Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.40to0.60 | % |
Density | | ISO1183 | 1.21 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 96.0 | Mpa |
Tensile Modulus | | ISO527-2/1 | 3300 | Mpa |
Flexural Modulus | | ISO178 | 3200 | Mpa |
Tensile Stress | 屈服 | ISO527-2/50 | 62.0 | Mpa |
Tensile Stress | 断裂 | ISO527-2/50 | 48.0 | Mpa |
Tensile Strain | 屈服 | ISO527-2/50 | 2.0 | % |
Tensile Strain | 断裂 | ISO527-2/50 | 30 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 91.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 80.0 | °C |
Vicat Softening Temperature | | ISO306/B50 | 94.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | | ISO179 | 10 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.