PC/ABS LEXAN™ FXE1414L-955 SABIC INNOVATIVE NANSHA

Unit Price:
$2388 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	11	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Moisture Absorption	Saturation, 23°C	ISO 62	0.17	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.070	%
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	2030	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2000	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.0	%
	Tensile Elongation	Yield	ISO 527-2/50	5.0	%
		Tensile Elongation	Break 3	ASTM D638	84	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	75	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2050	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2110	Mpa
Tensile Strength	Yield 3	ASTM D638	52.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	52.0	Mpa
		Tensile Strength	Break 3	ASTM D638	54.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	47.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	83.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	86.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D15259, ISO 306/B509	138	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	146	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	7.0E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	8.2E-5	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	118	°C

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Rear Temperature	260 到 280	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Hopper Temperature	60 到 80	°C
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	68.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.40 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.