Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30到0.50 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.40到0.60 | % |
Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 16 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield | ASTMD638 | 63.4 | Mpa |
Tensile Strength | Break | ASTMD638 | 49.0 | Mpa |
Tensile Elongation | Yield | ASTMD638 | 3.6 | % |
Tensile Elongation | Break | ASTMD638 | 80 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 3140 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 106 | Mpa |
Tensile Modulus | | ASTMD638 | 3520 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTI | | UL746 | 90.0 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 92.2 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 82.2 | °C |
Vicat Softening Temperature | | ASTMD15256 | 102 | °C |
RTIElec | | UL746 | 90.0 | °C |
Evolution Calendar intelligent importer | | UL746 | 85.0 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 5.9E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831 | 6.7E-05 | cm/cm/°C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 1900 | J/m |
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 47.5 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.19mm | UL94 | V-0 | |
UL flame retardant rating | 1.98mm | UL94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.