PC/ABS LUPOY® HR-5007AE LG GUANGZHOU
34
- Unit Price:
- $4347 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm,InjectionMolded | ASTMD955 | 0.50to0.80 | % |
| Moisture Absorption | Saturation | ISO622 | 0.15 | % |
| Melt Mass-Flow Rate | 250°C/2.16kg | ASTMD1238 | 5.3 | g/10min |
| Melt Volume flow Rate | 260°C/5.0kg | ASTMD1505 | 18.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | 3.20mm,InjectionMolded | ASTMD790 | 2110 | Mpa |
| Flexural Strength | 3.20mm | ASTMD790 | 77.5 | Mpa |
| Tensile Strength | Yield,3.20mm,Injection | ASTMD638 | 56.9 | Mpa |
| Tensile Strain | Break,3.20mm,InjectionMolded | ASTMD638 | >100 | % |
| Nominalstrainatbreak | ISO527-22 | >50 | % | |
| Tensile Modulus | ISO527-22 | 2200 | Mpa | |
| Tensile Stress | Yield | ISO527-22 | 60.0 | Mpa |
| Tensile Strain | Yield | ISO527-22 | 4.9 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm,InjectionMolded | ASTMD648 | 113 | °C |
| 1.8MPa | ISO75-22 | 104 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-22 | 7.7E-05 | cm/cm/°C |
| TD | ISO11359-22 | 8.3E-05 | cm/cm/°C | |
| Vicat Softening Temperature | 50N | ISO3062 | 119 | °C |
| Glass Transition Temperature | ISO11357-22 | 150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High Amp Arc Ignition | PLC | UL746 | PLC6 | |
| Electric strength | IEC60243-12 | 42 | KV/mm | |
| Comparative Tracking Index | CTI | UL746 | PLC0 | |
| Comparative Tracking Index | ISO 2577 | 200 | ||
| High Amp Arc Ignition | 1.6mm | UL746 | PLC1 | |
| 3.0mm | UL746 | PLC1 | ||
| Hot-wire Ignition | 1.6mm | UL746 | PLC3 | |
| 3.0mm | UL746 | PLC3 | ||
| Relative Permittivity | 1MHz | ASTM D1646 | 2.80 | |
| Surface Resistivity | IEC600932 | 3.8E+14 | ohms | |
| Arc Resistance | ASTMD495 | PLC6 | ||
| Volume Resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Dissipation Factor? | 1MHz | ASTM D1646 | 0.010 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA2 | NoBreak | |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eU2 | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 114 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.