Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40to0.60 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.40to0.60 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.40 | % |
Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 22 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 100mmSpan | ASTMD790 | 2590 | Mpa |
Tensile Strength | Yield | ASTMD638 | 64.1 | Mpa |
Tensile Elongation | Yield | ASTMD638 | 5.0 | % |
Tensile Elongation | Break | ASTMD638 | 40 | % |
Flexural Strength | Yield,100mmSpan | ASTMD790 | 96.5 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-30to30°C | ASTMD696 | 7.2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-30to30°C | ASTMD696 | 7.2E-05 | cm/cm/°C |
Vicat Softening Temperature | | ASTMD15254 | 113 | °C |
Thermal Conductivity | | ASTMC177 | 0.20 | W/m/K |
RTIElec | | UL746 | 85.0 | °C |
Evolution Calendar intelligent importer | | UL746 | 85.0 | °C |
RTIStr | | UL746 | 85.0 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 102 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 87.8 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 93.3 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | >1.0E+16 | ohms |
Dielectric Constant | 50Hz | ASTMD150 | 2.80 | |
Dielectric Constant | 60Hz | ASTMD150 | 2.80 | |
Dielectric Constant | 1MHz | ASTMD150 | 2.70 | |
Volume Resistivity | | ASTMD257 | 1.6E+17 | ohms·cm |
Dissipation Factor? | 50Hz | ASTMD150 | 5.2E-03 | |
Dissipation Factor? | 60Hz | ASTMD150 | 5.2E-03 | |
Dissipation Factor? | 1MHz | ASTMD150 | 7.1E-03 | |
Hot-wire Ignition | HWI | UL746 | PLC2 | |
Dielectric Strength | 3.20mm,inOil | ASTMD149 | 24 | KV/mm |
Comparative Tracking Index | CTI | UL746 | PLC2 | |
Arc Resistance | | ASTMD495 | PLC6 | |
High Amp Arc Ignition | HAI | UL746 | PLC0 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 121 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ASTMD2863 | 30 | % |
UL flame retardant rating | 0.76mm | UL94 | V-2 | |
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 2.5mm | UL94 | 5VB | |
UL flame retardant rating | 3.4mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.