PC/ABS INFINO® NH-1017 Samsung Cheil South Korea
130
- Unit Price:
- $3891 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance high strength
- Application Areas:--
- Color:--
- Grade:Halogen-free flame retardant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃/10.0 kg | ASTM D1238 | 55 | g/10 min |
| Shrinkage rate | Flow | ASTM D955 | 0.50 to 0.7 | % |
| Rockwell hardness | R-Scale | ASTM D785 | 114 | |
| Density/specific gravity | ASTM D792 | 1.18 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| IZOD notch impact strength | 3.18mm | ASTM D256 | --- | J/m |
| tensile strength | Yield | ASTM D638 | 59 | Mpa |
| Bending modulus | ASTM D790 | 2450 | Mpa | |
| bending strength | ASTM D790 | 78.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa,Unannealed，6.35 mm | ASTM D648 | 85 | °C |
| Vicat softening temperature | ISO 306/B50 | 95 | °C |
| other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | 2.00 mm | UL 94 | V0 | |
| 3.00mm | UL 94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.