PC/ABS CYCOLAC™ C1200HF-BK1065 SABIC INNOVATIVE US
85
- Unit Price:
- $2281 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance heat-resisting
- Application Areas:Electrical field Electronic field Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 19 | g/10 min |
| Melt Volume flow Rate | 265°C/5.0 kg | ISO 1133 | 24.0 | cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2270 | Mpa |
| -- | ISO 527-2/1 | 2360 | Mpa | |
| Tensile Elongation | Yield 3 | ASTM D638 | 5.0 | % |
| Yield | ISO 527-2/50 | 4.8 | % | |
| Break 3 | ASTM D638 | 150 | % | |
| Break | ISO 527-2/50 | 110 | % | |
| Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 2340 | Mpa |
| -- | ISO 178 | 2250 | Mpa | |
| Tensile Strength | Yield 3 | ASTM D638 | 57.0 | Mpa |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Flexural Stress | -- | ISO 178 | 86.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 88.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 105 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 105 | °C | |
| Vicat Softening Temperature | ISO 306/B50 | 130 | °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 to 40°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 129 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Bf | 130 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 112 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 2 | ||
| High Amp Arc Ignition | UL 746 | PLC 1 | ||
| Hot-wire Ignition | UL 746 | PLC 3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hopper Temperature | 60 到 80 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 30 到 80 | % | ||
| Rear Temperature | 250 到 290 | °C | ||
| Middle Temperature | 255 到 295 | °C | ||
| Front Temperature | 260 到 300 | °C | ||
| Nozzle Temperature | 275 到 300 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.038 到 0.076 | mm | ||
| Drying Temperature | 100 到 110 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 275 到 300 | °C | ||
| Mold Temperature | 60 到 90 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 54.0 | J |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.2 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.