Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | 23°C | ISO1183 | 1.18 | g/cm³ |
Melt Volume flow Rate | 240°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
Modeling Shrinkage | TD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
Modeling Shrinkage | MD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Melt Viscosity | 260°C | ISO11443-A | 160 | Pa·s |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break,23°C | ISO527-2/50 | 45.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2/50 | 3.5 | % |
Tensile Strain | Break,23°C | ISO527-2/50 | >40 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 2700 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2/50 | 60.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 7.6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 92.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 82.0 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 95.0 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 97.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
Relative Permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
Relative Permittivity | 23°C,1MHz | IEC60250 | 3.10 | |
Dissipation Factor? | 23°C,100Hz | IEC60250 | 5E-03 | |
Dissipation Factor? | 23°C,1MHz | IEC60250 | 6E-03 | |
Comparative Tracking Index | SolutionA | IEC60112 | 350 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -30°C | ISO180/A | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/A | 35 | kJ/m² |
Notched Izod impact strength | 23°C | ISO180 | NoBreak | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 2.0mm | UL94 | 5VB | |
UL flame retardant rating | 3.0mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.