PC/ABS INFINO® NH1017T Samsung Cheil South Korea
92
- Unit Price:
- $4222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance Aging resistance
- Application Areas:tubing Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.18 | ||
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 60 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 55 | g/10min |
| 220°C/10.0kg | ISO1133 | 55 | g/10min | |
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.20to0.30 | % |
| TD：3.20mm | ASTMD955 | 0.20to0.40 | % | |
| TD:3.20mm | ISO2577 | 0.20to0.40 | % | |
| MD:3.20mm | ISO2577 | 0.20to0.30 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO527-2/50 | 59.0 | Mpa |
| Break | ISO527-2/50 | 44.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | 10 | % |
| Tensile Modulus | ISO527-2/50 | 2400 | Mpa | |
| Tensile Strength | ASTM D638/ISO 527 | 610 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell Hardness | ASTM D785 | 120 | ||
| Flexural Modulus | ASTM D790/ISO 178 | 24000 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 870 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTMD790 | 2100 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 43.0 | Mpa |
| Yield | ASTMD638 | 53.0 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 8.8 | % |
| Flexural Strength | ASTMD790 | 74.0 | Mpa | |
| Flexural Stress | ISO178 | 83.0 | Mpa | |
| Tensile Modulus | ASTMD638 | 2400 | Mpa | |
| Flexural Modulus | ISO178 | 2350 | Mpa | |
| Izod notch impact strength | ASTM D256/ISO 179 | 50 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO306/B50 | 91.0 | °C | |
| Burning Rate | UL94 | 2.0, 3.0 | ||
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 87.0 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 85.0 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 80.0 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 75.0 | °C | |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 98 | ℃（℉） | |
| RTIElec | 2.0mm | UL746 | 85.0 | °C |
| Evolution Calendar intelligent importer | 2.0mm | UL746 | 85.0 | °C |
| RTIStr | 2.0mm | UL746 | 85.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 13 | kJ/m² |
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 14 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 113 | |
| R-Scale | ISO2039-2 | 113 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 2.0to3.0mm | UL94 | V-05VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.