Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 18 | g/10min |
Melt Volume flow Rate | 220°C/5.0kg | ISO1133 | 14.0 | cm3/10min |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30到0.50 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.40到0.60 | % |
-- | | ASTMD792 | 1.26 | g/cm³ |
-- | | ISO1183 | 1.25 | g/cm³ |
Equilibrium,23°C,50%RH | | ISO62 | 0.010 | % |
24hr,50%RH | | ASTMD570 | 0.010 | % |
24hr | | ASTMD570 | 0.10 | % |
Saturation ,23℃ | | ISO62 | 0.090 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Yield | | ASTMD638 | 4.0 | % |
Break | | ASTMD638 | 50.0 | Mpa |
Yield | | ASTMD638 | 65.0 | Mpa |
Break | | ASTMD638 | 100 | % |
50.0mm Span | | ASTMD790 | 3300 | Mpa |
Yield,50.0mm Span | | ASTMD790 | 100 | Mpa |
--9 | | ISO178 | 97.0 | Mpa |
--8 | | ISO178 | 3450 | Mpa |
--1 | | ASTMD638 | 3500 | Mpa |
Yield | | ASTMD638 | 65.0 | Mpa |
yield | | ISO527-2/5 | 3.5 | % |
fracture | | ISO527-2/5 | 50.0 | Mpa |
fracture | | ISO527-2/50 | 15 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 83.0 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831,ISO11359-2 | 5.5E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831,ISO11359-2 | 6E-05 | cm/cm/°C |
-- | | ASTMD152515 | 91.0 | °C |
-- | | ISO306/B50 | 98.0 | °C |
-- | | ISO306/B120 | 102 | °C |
1.8MPa, Unannealed,6.40mm | | ASTMD648 | 89.0 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 80.0 | °C |
0.45MPa, Unannealed,6.40mm | | ASTMD648 | 97.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 3.5E+15 | ohms |
Volume Resistivity | | ASTMD257 | 2.7E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
-30°C12 | | ISO180/1A | 5.0 | kJ/m² |
23°C13 | | ISO180/1A | 10 | kJ/m² |
-30°C | | ASTMD256 | 88 | J/m |
23°C | | ASTMD256 | 200 | J/m |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.600mm | UL94 | V-1 | |
UL flame retardant rating | 0.800mm | UL94 | V-0 | |
UL flame retardant rating | 1.50mm | UL94 | 5VB | |
Glow Wire Flammability Index | 0.800mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 850 | °C |
Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 800 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.