PC/ABS CYCOLAC™ C1200HF SABIC INNOVATIVE US
34
- Unit Price:
- $2619 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 61MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50to0.70 | % |
Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 19 | g/10min |
Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
Density / Specific Gravity | ASTMD792 | 1.15 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flexural Stress | ISO178 | 86.0 | Mpa | |
Tensile Elongation | Break | ASTMD638 | 150 | % |
Tensile Modulus | ISO527-2/1 | 2370 | Mpa | |
Flexural Modulus | ISO178 | 2250 | Mpa | |
Tensile Stress | Yield | ISO527-2/50 | 55.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 4.8 | % |
Break | ISO527-2/50 | 110 | % | |
Tensile Elongation | Yield | ASTMD638 | 5.0 | % |
Tensile Modulus | ASTMD638 | 2280 | Mpa | |
Tensile Strength | Yield | ASTMD638 | 57.2 | Mpa |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 88.3 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
RTIElec | UL746 | 105 | °C | |
Evolution Calendar intelligent importer | UL746 | 80.0 | °C | |
RTIStr | UL746 | 105 | °C | |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 129 | °C |
1.8MPa,Unannealed,3.20mm | ASTMD648 | 113 | °C | |
Vicat Softening Temperature | ISO306/B50 | 130 | °C | |
Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 | °C |
1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 110 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Hot-wire Ignition | HWI | UL746 | PLC3 | |
High Amp Arc Ignition | HAI | UL746 | PLC1 | |
Comparative Tracking Index | CTI | UL746 | PLC2 |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Notched Izod Impact Strength | -30°C | ISO180/1A | 34 | kJ/m² |
23°C | ISO180/1A | 49 | kJ/m² | |
Notched Izod Impact Strength | -30°C | ASTMD256 | 480 | J/m |
23°C | ASTMD256 | 590 | J/m | |
Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 54.2 | J |
23°C,TotalEnergy | ASTMD3763 | 54.2 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 1.2mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.