Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.18 | |
Modeling Shrinkage | | ASTM D955 | 0.4-0.6 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.5 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 26 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.18mm | ASTMD955 | 1.7 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.050 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | >50 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 2700 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 60 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | Break | ASTMD638 | 9.0 | % |
Flexural Modulus | | ASTMD790 | 1070 | Mpa |
Tensile Strength | Break | ASTMD638 | 24.1 | Mpa |
Izod notch impact strength | | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 82.2 | °C |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 92 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.76 | mm/mm.℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | | ASTM D150/IEC 60250 | 3.2 | |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.1 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 105 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.