PC CALIBRE™ MEGARAD™ 2081-15 STYRON US
172
- Unit Price:
- $5648 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medical grade
- Application Areas:Nursing supplies Medical supplies
- Color:--
- Grade:Medical grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 0.50到0.70 | % |
| MD | ISO294-4 | 0.50到0.70 | % | |
| Water absorption rate | 23°C,24hr | ASTMD570,ISO62 | 0.15 | % |
| Equilibrium,23°C,50%RH | ASTMD570,ISO62 | 0.32 | % | |
| Melt volume flow rate | 300°C/1.2kg | ISO11334 | 12.0 | cm3/10min |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238,ISO1133 | 15 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Wear resistance | ASTMD1044 | 45 | % | |
| Tensile strength | Break5 | ASTMD638 | 68.3 | Mpa |
| Break | ISO527-2/50 | 68.0 | Mpa | |
| Yield5 | ASTMD638 | 62.1 | Mpa | |
| Yield | ISO527-2/50,ISO527-24 | 62.0 | Mpa | |
| Tensile modulus | --5 | ASTMD638 | 2210 | Mpa |
| -- | ISO527-2/50,ISO527-24 | 2300 | Mpa | |
| elongation | Yield5 | ASTMD638 | 6.0 | % |
| Yield | ISO527-2/50,ISO527-24 | 6.0 | % | |
| Break5 | ASTMD638 | 150 | % | |
| Break | ISO527-2/50 | 150 | % | |
| Break | ISO527-24 | >50 | % | |
| Bending modulus | --6 | ASTMD790 | 2410 | Mpa |
| --7,8 | ISO178 | 2400 | Mpa | |
| bending strength | --6 | ASTMD790 | 96.5 | Mpa |
| --7,8 | ISO178 | 98.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Annealed | ASTMD648 | 139 | °C |
| 0.45MPa | ISO75-24 | 137 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 122 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 120 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 136 | °C | |
| 1.8MPa | ISO75-24 | 123 | °C | |
| Vicat softening temperature | -- | ASTMD152510 | 148 | °C |
| -- | ISO306/B50 | 143 | °C | |
| 50°C/h,B(50N) | ISO3064 | 143 | °C | |
| Linear coefficient of thermal expansion | MD：-40to82°C | ASTMD696 | 6.8E-05 | cm/cm/°C |
| MD：-- | ISO 178/1993 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | ASTMD1494,IEC60243-14 | 17 | KV/mm | |
| Dissipation factor | 50Hz | ASTMD150 | 1E-03 | |
| 1MHz | ASTMD150,IEC602504 | 2E-03 | ||
| 100Hz | IEC602504 | 1E-03 | ||
| Dielectric constant | 60Hz | ASTMD150 | 3.00 | |
| 1MHz | ASTMD150,IEC602504 | 3.00 | ||
| 100Hz | IEC602504 | 3.00 | ||
| Volume resistivity | -- | ASTMD257 | 2E+17 | ohms·cm |
| -- | IEC600934 | >1.0E+13 | ohms·m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile impact strength | ASTMD1822 | 378 | kJ/m² | |
| Charpy impact strength | -30°C | SK | 无断裂 | |
| 23°C | SK | 无断裂 | ||
| Dart impact equipped with measuring instruments 9 | 23°C,总能量 | ASTMD3763 | 81.3 | J |
| Cantilever beam without notch impact strength | 23°C | ASTMD256,ISO180 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 118 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542,ISO489 | 1.586 | ||
| transmissivity | ASTMD1003 | 89.0 | % | |
| Haze | ASTMD1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Normal combustion performance with a thickness of 1.6mm | 1.60mm,UL | ISO12104 | HB | |
| Flame retardant rating at a certain thickness and hour | 3.20mm,UL | ISO12104 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.