PC LEXAN™ CFR9111-NA8G001T SABIC INNOVATIVE NANSHA

Unit Price:
$4919 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Non chloro non bromine fl
Application Areas:Electrical appliances Electronic and Electrical Electronic display Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.55 到 0.75	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.60 到 0.80	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.13	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.11	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	17.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield 3	ASTM D638	67.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile Strength	Break 3	ASTM D638	54.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	57.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2400	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2300	Mpa
Tensile Elongation	Yield 3	ASTM D638	6.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	80	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	73	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2400	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2400	Mpa
Flexural Stress	-- 5, 6	ISO 178	96.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	103	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.8E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.7E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI		UL 746	130	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C
Vicat Softening Temperature	--	ASTM D152510	136	°C
	Vicat Softening Temperature	--	ISO 306/B50	139	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	140	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	130	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	131	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	121	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1.10 GHz	ASTM ES7-83	5.6E-3
Dielectric Constant	1.10 GHz	ASTM ES7-83	2.79

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	280 到 305	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	260 到 280	°C
Middle Temperature	270 到 295	°C
Front Temperature	280 到 305	°C
Nozzle Temperature	275 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	80.0	J
Unnotched Izod Impact Strength	-30°C	ASTM D4812, ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ASTM D4812, ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	59	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	1000 µm	内部方法	> 90.0	%
	Transmittance	2000 µm	内部方法	> 89.0	%
	Transmittance	Transmittance	3000 µm	内部方法	> 88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	850	°C
Flame Rating	0.40 mm	UL 94	V-2
	Flame Rating	1.2 mm	UL 94	V-1
	Flame Rating	Flame Rating	1.5 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.