Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ISO294-4 | 0.40to0.60 | % |
Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 15 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strength | 4.00mm,InjectionMolded | ISO178 | 105 | Mpa |
Tensile Strain | Yield,4.00mm,InjectionMolded | ISO527-2/50 | 4.0 | % |
Tensile Stress | Break,4.00mm,Injection | ISO527-2/50 | 50.0 | Mpa |
Tensile Strain | Break,4.00mm,Injection | ISO527-2/50 | 9.0 | % |
Flexural Modulus | 4.00mm,InjectionMolded | ISO178 | 3800 | Mpa |
Tensile Modulus | 4.00mm,InjectionMolded | ISO527-2/1 | 3950 | Mpa |
Tensile Modulus | 4.00mm,InjectionMolded | ISO527-2/50 | 4000 | Mpa |
Tensile Strength | Yield,4.00mm,InjectionMolded | ISO527-2/50 | 65.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 141 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 133 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ISO75-2/A | 139 | °C |
Vicat Softening Temperature | -- | ISO306/A120 | 155 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 145 | °C |
Ball Indentation Temperature | | IEC60335-1 | >130 | °C |
Linear thermal expansion coefficient | MD:-40to80°C | ASTMD696 | 1.5E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | 3.00mm,SolutionA | IEC60112 | 200 | V |
Dielectric Strength | 2.00mm | IEC60243-1 | >70 | KV/mm |
Dissipation Factor? | 2.00mm,50Hz | IEC60250 | 8E-03 | |
Dissipation Factor? | 2.00mm,1MHz | IEC60250 | 0.016 | |
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Dielectric Constant | 2.00mm,50Hz | IEC60250 | 3.00 | |
Dielectric Constant | 2.00mm,1MHz | IEC60250 | 3.10 | |
Volume Resistivity | 2.00mm | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C,InjectionMolded | ISO180/A | 9.0 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 29 | % |
Flame Rating | 1.5mm | UL94 | V-0 | |
Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 960 | °C |
Glow Wire Ignition Temperature | 2.0mm | IEC60695-2-13 | 960 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.