PC INFINO® NH-3200 FW9661 Samsung Cheil South Korea
80
- Unit Price:
- $3945 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant
- Application Areas:Laptop Electronic and Electrical Audio and video equipment
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | ASTM D955 | 0.10 到 0.40 | % |
| Across Flow : 3.20 mm | ASTM D955 | 0.10 到 0.40 | % | |
| Across Flow : 2.00 mm | ISO 294-4 | 0.10 到 0.40 | % | |
| 流量 : 2.00 mm | ISO 294-4 | 0.10 到 0.40 | % | |
| Melt Mass-Flow Rate | 250°C/5.0 kg | ASTM D1238, ISO 1133 | 19 | g/10 min |
| 300°C/1.2 kg | ASTM D1238, ISO 1133 | 12 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 3 | ASTM D638 | 4900 | Mpa |
| -- | ISO 527-2/5 | 5000 | Mpa | |
| Tensile Elongation | Break 3 | ASTM D638 | 3.0 | % |
| Break | ISO 527-2/5 | 3.0 | % | |
| Flexural Modulus | -- 4 | ASTM D790 | 5900 | Mpa |
| -- 5 | ISO 178 | 6000 | Mpa | |
| Flexural Strength | -- 4 | ASTM D790 | 150 | Mpa |
| -- 5 | ISO 178 | 150 | Mpa | |
| Tensile Strength | Yield 3 | ASTM D638 | 120 | Mpa |
| Yield | ISO 527-2/5 | 120 | Mpa | |
| Break 3 | ASTM D638 | 120 | Mpa | |
| Break | ISO 527-2/5 | 120 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 105 | °C |
| 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 102 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 100 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 97.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rear Temperature | 260 到 270 | °C | ||
| Middle Temperature | 270 到 290 | °C | ||
| Front Temperature | 260 到 280 | °C | ||
| Nozzle Temperature | 270 | °C | ||
| Back Pressure | 0.981 到 1.96 | Mpa | ||
| Screw Speed | 30 到 100 | rpm | ||
| Injection Pressure | 98.1 | Mpa | ||
| Desiccant Dryer | 3.0 到 4.0 | hr | ||
| 80 | °C | |||
| vacuum dryer | 80 | °C | ||
| 4.0 到 6.0 | hr | |||
| Suggested Max Moisture | 0.040 | % | ||
| Mold Temperature | 60 到 70 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 120 | |
| R -Sale | ISO 2039-2 | 120 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.75 mm | UL 94 | V-0 | |
| 0.8 to 3.0 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.