PC LEXAN™ DMX1435-GY6E563T SABIC INNOVATIVE SINGAPHORE
85
- Unit Price:
- $10581 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Scratch resistant High temperature resistan high strength
- Application Areas:Wire and cable Electronic and electrical Automotive components
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow3.2mm | 内部测试方法 | 0.5-0.8 | % |
| Moisture Absorption | 24hr | ASTM D570 | 0.08 | % |
| 23℃Equilibrium | ASTM D570 | 0.28 | % | |
| 50RHEquilibrium | ASTM D570 | 0.13 | % | |
| 50RH 24hr | ASTM D570 | 0.04 | % | |
| 23℃Saturation | ISO 62 | 0.27 | % | |
| 23℃ 50RH | ISO 62 | 0.13 | % | |
| Melt index | 300℃ 1.2kg | ASTM D1238 | 14.5 | g/10min |
| 300℃ 1.2kg | ISO 1133 | 13 | cm3/10min | |
| Specific Volume | ASTM D792 | 0.85 | cm³/g | |
| proportion | ASTM D792 | 1.2 | g/cm³ | |
| ISO 1183 | 1.17 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C3.0mm 1eA型 | ISO 179 | 3 | kJ/m² |
| Unnotched Izod Impact Strength | -30℃ 3.0mm | ISO 180 | 45 | kJ/m² |
| Charpy Notched Impact Strength | 30℃ 3.0mm 1eA型^ | ISO 179 | 3 | kJ/m² |
| Taber Abrasion Resistance | CS-17轮1kg | ASTM D1044 | 10 | mg/1000cy |
| Taber Abrasion Resistance | CS-17轮1kg | 内部测试方法 | 10 | mg/1000cy |
| ericksen scratch depth | 6N | 内部测试方法 | 14 | micrometer |
| Instrumented Dart Impact | 23℃总能量 | ASTM D3763 | 30 | J |
| Notched Izod Impact Strength | 23℃ | ASTM D256 | 30 | J/m |
| -30℃ | ASTM D256 | 30 | J/m | |
| 23°C 3.0mm A型Notched | ISO 180 | 5 | kJ/m² | |
| “-30℃ 3.0mm A型Notched | ISO 180 | 4 | kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C 3.0mm | ISO 179 | NB | kJ/m² |
| -30℃ 3.0mm | ISO 179 | 47 | kJ/m² | |
| Unnotched Izod Impact Strength | 23℃ | ASTM D4812 | NB | J/m |
| 23°C 3.0mm | ISO 180 | NB | kJ/m² | |
| Tensile Modulus | 50mm/min | ASTM D638 | 2900 | Mpa |
| 1.0mm/min | ISO 527 | 2450 | Mpa | |
| Tensile Strength | Yield50mm/min I型 | ASTM D638 | 80 | Mpa |
| Break50mm/mini型 | ASTM D638 | 65 | Mpa | |
| Yield50mm/min | ISO 527 | 80 | Mpa | |
| 斯裂50mm/min | ISO 527 | 60 | Mpa | |
| Tensile Elongation | Yield50mm/min iI型 | ASTM D638 | 7 | % |
| Break50mm/min I型 | ASTM D638 | 70 | % | |
| Yield50mm/min | ISO 527 | 7 | % | |
| Break50mm/min | ISO 527 | 40 | % | |
| Flexural Modulus | 1.3mm/min | ASTM D790 | 2600 | Mpa |
| 2.0mm/min | ISO 178 | 2450 | Mpa | |
| Flexural Strength | Yield1.3mm/min | ASTM D790 | 120 | Mpa |
| Yield2.0mm/min | ISO 178 | 108 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | Unannealed0.45MPa 3.2mm | ASTM D648 | 133 | °C |
| Unannealed1.8MPa 3.2mm | ASTM D648 | 119 | °C | |
| 0.45MPa 4.0mm | ISO 75 | 131 | °C | |
| 1.8MPa 4.0mm | ISO 75 | 118 | °C | |
| Vicat Softening Temperature | 50℃/hr 50N | ASTM DI 525 | 139 | °C |
| 50℃/hr 50N | ISO 306 | 138 | °C | |
| 120℃/hr 50N | ISO 306 | 140 | °C | |
| Coefficient of Linear Thermal Expansion | Flow23~80℃ | ISO 11359 | 0.000070 | cm/cm/℃ |
| 垂直23~80℃ | ISO 11359 | 0.000070 | cm/cm/℃ | |
| Thermal Conductivity | ASTM C177 | 0.2 | w/(m.℃) | |
| ISO 8302 | 0.2 | w/(m.℃) | ||
| Ball Indentation Hardness | IEC 60695 | 125 | °C | |
| IEC 60695 | 140 | °C | ||
| Coefficient of Linear Thermal Expansion (Flow) | -40.0~95℃ | ASTM E831 | 0.000070 | cm/cm/℃ |
| Coefficient of Linear Thermal Expansion | -40.0~95℃ | ASTM E831 | 0.000070 | cm/cm/℃ |
| Specific Heat | ASTM C351 | 1.4 | J/(g.℃) |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Pencil Hardness | 1.0kg | ASTM D3363 | H | |
| Rockwell Hardness | L标尺 | ASTM D785 | 108 | |
| M标尺 | ASTM D785 | 93 | ||
| Ball Indentation Hardness | H358/30 | ISO 2039 | 128 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | 2540pm | ASTM DI 003 | 88 | % |
| Haze | 2540Pm | ASTM D1003 | 0.8 | % |
| Refractive index of light | ASTM D542 | 1.584 | ||
| ISO 489 | 1.584 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.