PC LEXAN™ XHT3141-GY8DO46 SABIC INNOVATIVE NANSHA
75
- Unit Price:
- $4590 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan
- Application Areas:Automotive interior parts
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.30 | % | |
| Melt Mass-Flow Rate | 330°C/2.16 kg | ASTM D1238 | 33 | g/10 min |
| Melt Volume flow Rate | 330°C/2.16 kg | ISO 1133 | 30.0 | cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.60 到 0.90 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 5, 6 | ISO 178 | 80.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 120 | Mpa | |
| Tensile Strength | Yield 3 | ASTM D638 | 70.0 | Mpa |
| Yield | ISO 527-2/50 | 70.0 | Mpa | |
| Break 3 | ASTM D638 | 55.0 | Mpa | |
| Break | ISO 527-2/50 | 60.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 2700 | Mpa |
| -- | ISO 527-2/1 | 2500 | Mpa | |
| Tensile Elongation | Yield 3 | ASTM D638 | 6.0 | % |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Break 3 | ASTM D638 | 70 | % | |
| Break | ISO 527-2/50 | 70 | % | |
| Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 2600 | Mpa |
| -- 5 | ISO 178 | 2500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B12010 | 170 | °C |
| -- | ISO 306/B50 | 168 | °C | |
| Thermal Conductivity | 25°C | ASTM C177 | 0.20 | W/m/K |
| RTI | UL 746 | 150 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 150 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 6.0E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.0E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 6.0E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 166 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Bf | 164 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 156 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 152 | °C | |
| Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 23 | KV/mm |
| Comparative Tracking Index | UL 746 | PLC 3 | ||
| Hot-wire Ignition | UL 746 | PLC 3 | ||
| High Amp Arc Ignition | UL 746 | PLC 0 | ||
| Dissipation Factor? | 100 Hz | ASTM D150 | 0.031 | |
| 1 MHz | ASTM D150 | 0.011 | ||
| Surface Resistivity | ASTM D257 | > 1.0E+17 | ohms | |
| Dielectric Constant | 100 Hz | ASTM D150 | 2.90 | |
| 1 MHz | ASTM D150 | 2.80 | ||
| Volume Resistivity | ASTM D257 | > 1.0E+17 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 135 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 290 到 350 | °C | ||
| Mold Temperature | 95 到 130 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 270 到 330 | °C | ||
| Middle Temperature | 280 到 340 | °C | ||
| Front Temperature | 290 到 350 | °C | ||
| Nozzle Temperature | 285 到 345 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 90 | rpm | ||
| Vent Depth | 0.025 到 0.080 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 68.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 3.0 mm | IEC 60695-2-12 | 960 | °C |
| Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 875 | °C |
| Flame Rating | 1.5 mm | UL 94 | HB | |
| 3.0 mm | UL 94 | HB | ||
| Metallized Haze Onset | 内部方法 | 165 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.