Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ISO294-4 | 0.60 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.35 | % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 26.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | >50 | % |
| Flexural Stress | | ISO178 | 90.0 | Mpa |
| Tensile Stress | Yield | ISO527-2 | 60.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 5.0 | % |
| Tensile Modulus | | ISO527-2 | 2500 | Mpa |
| Flexural Modulus | | ISO178 | 2400 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 104 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1.00GHz | IEC60250 | 5E-03 | |
| Relative Permittivity | 1.00GHz | IEC60250 | 3.00 | |
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 1.5mm | IEC60695-11-10,-20 | V-0 | |
| Flammability level | 1.0mm | IEC60695-11-10,-20 | V-1 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.