Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.50to0.70 | % |
Moisture Absorption | 23°C,24hr | ASTMD570 | 0.15 | % |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
Outdoor Suitability | | UL746C | f1 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield | ASTMD638 | 61.4 | Mpa |
Tensile Strength | Break | ASTMD638 | 58.6 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 59.0 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 61.0 | Mpa |
Tensile Modulus | | ASTMD638 | 2380 | Mpa |
Tensile Elongation | Break | ASTMD638 | 120 | % |
Tensile Elongation | Yield | ASTMD638 | 6.0 | % |
Flexural Modulus | | ASTMD790 | 2330 | Mpa |
Flexural Strength | | ASTMD790 | 97.9 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 137 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 127 | °C |
RTIElec | | UL746 | 130 | °C |
Evolution Calendar intelligent importer | | UL746 | 115 | °C |
RTIStr | | UL746 | 130 | °C |
Linear thermal expansion coefficient | MD | ASTMD696 | 6.5E-05 | cm/cm/°C |
Vicat Softening Temperature | | ASTMD1525 | 151 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Hot-wireIgnition | 0.9to3.0mm | UL746 | PLC2 | |
High Amp Arc Ignition | PLC | UL746 | PLC1 | |
Comparative Tracking Index | CTI | UL746 | PLC2 | |
High Amp Arc Ignition | 0.9mm | UL746 | PLC2 | |
High Amp Arc Ignition | 1.0to3.0mm | UL746 | PLC1 | |
Arc Resistance | | ASTMD495 | PLC7 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Impact Strength | | ASTMD1822 | 630 | kJ/m² |
Instrumented Dart Impact | | ASTMD3763 | 62.1 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.9mm,all | 内部方法 | V-1 | |
Flame Rating | 0.9mm,wt,black | 内部方法 | V-0 | |
Flame Rating | 1.0mm,all | 内部方法 | V-0 | |
Flame Rating | 2.0mm,all | 内部方法 | 5VB | |
Flame Rating | 3.0mm,all | 内部方法 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.