Unit Price:
$3666 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Easy to form Short molding cycle Low temperature and high
Application Areas:Electrical appliances Electronic display Architectural Application Lighting applications
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%
Melt Mass-Flow Rate	260°C/2.16 kg	ASTM D1238	7.0	g/10 min
Melt Volume flow Rate	260°C/5.0 kg	ISO 1133	18.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	90.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	95.0	Mpa
Tensile Strength	Yield 3	ASTM D638	62.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	62.0	Mpa
		Tensile Strength	Break 3	ASTM D638	54.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	58.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2500	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2350	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.0	%
	Tensile Elongation	Yield	ISO 527-2/50	5.0	%
		Tensile Elongation	Break 3	ASTM D638	100	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	100	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2600	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2350	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D15259, ISO 306/B509	134	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	135	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	7.7E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	7.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	5.9E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	7.0E-5	cm/cm/°C
RTI		UL 746	100	°C
RTI Imp		UL 746	100	°C
RTI Elec		UL 746	100	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	128	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 8	ISO 75-2/Be	125	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	114	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	119	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 8	ISO 75-2/Ae	115	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	3.20 mm, in Oil	ASTM D149	27	KV/mm
Comparative Tracking Index		IEC 60112	250	V
Comparative Tracking Index		UL 746	PLC 2
Hot-wire Ignition		UL 746	PLC 3
High Amp Arc Ignition		UL 746	PLC 1
Volume Resistivity		IEC 60093	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	90 到 100	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	270 到 300	°C
Mold Temperature	60 到 90	°C
Hopper Temperature	60 到 80	°C
Drying Time	2.0 到 4.0	hr
Rear Temperature	230 到 260	°C
Middle Temperature	250 到 290	°C
Front Temperature	260 到 300	°C
Nozzle Temperature	250 到 290	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	72.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	800	°C
	Glow Wire Ignition Temperature	2.0 mm	IEC 60695-2-13	800	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	800	°C
Flame Rating	1.5 mm	UL 94	V-0
	Flame Rating	2.0 mm	UL 94	5VB
		Flame Rating	3.0 mm	UL 94	5VA
		Flame Rating	Flame Rating	3.0 mm, Testing by SABIC	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.