PC 8000-05 LG CHEM KOREA
91
- Unit Price:
- $3043 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High rigidity
- Application Areas:Electrical applications Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570, ISO 62 | 0.12 | % |
| Equilibrium, 23°C, 50% RH | ASTM D570, ISO 62 | 0.20 | % | |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 3.5 | g/10 min |
| Shrinkage rate - flow | ASTM D955 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield, 23°C 2 | ASTM D638 | 58.0 | Mpa |
| Yield, 23°C | ISO 527-2/50 | 57.0 | Mpa | |
| Break | ASTM D638 | 68.0 | Mpa | |
| Break | ISO 527-2 | 64.0 | Mpa | |
| Tensile modulus | -- | ASTM D638 | 2180 | Mpa |
| -- | ISO 527-2 | 2390 | Mpa | |
| elongation | Yield | ASTM D638, ISO 527-2 | 6.0 | % |
| Break | ASTM D638 | 120 | % | |
| Break | ISO 527-2 | 110 | % | |
| Bending modulus | -- | ASTM D790 | 2030 | Mpa |
| -- | ISO 178 | 1940 | Mpa | |
| bending strength | -- | ASTM D790 | 86.0 | Mpa |
| -- | ISO 178 | 82.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ISO 306/B120, ASTM D15254 | 138 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Annealed, 4.00 mm | ASTM D648 | 132 | °C |
| 1.8 MPa, Unannealed, 4.00 mm | ASTM D648 | 118 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 115 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | ASTM D648 | 130 | °C | |
| Linear coefficient of thermal expansion - flow | -40 to 82°C | ASTM D696 | 7.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D256, ISO 180 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 50 | |
| R-Scale | ASTM D785 | 120 | ||
| M -Sale | ISO 2039-2 | 50 | ||
| R -Sale | ISO 2039-2 | 120 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 3000 µm | ASTM D1003 | > 88.0 | % |
| 3000 µm | ISO 13468-1 | > 88.0 | % | |
| Haze | 3000 µm | ASTM D1003 | < 1.0 | % |
| 3000 µm | ISO 14782 | < 1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.