Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 280℃/2.16 kg | ISO 1133 | 17 | g/10 min |
Modeling Shrinkage | Across Flow : 4.00 mm | ISO 294-4 | 0.5-0.7 | % |
Modeling Shrinkage | 流量 : 4.00 mm | ISO 294-4 | 0.5-0.7 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength(Yield) | | ISO 527-2/50 | 60 | Mpa |
Moisture Absorption | 23℃, 24 hr | ISO 62 | 0.22 | % |
Tensile Elongation?(Break) | | ISO 527-2/50 | 100 | % |
Tensile Elongation?(Break) | | ISO 527-2/50 | 50 | % |
Tensile Modulus | | ISO 527-2/1 | 2350 | Mpa |
Flexural Modulus | | ISO 178 | 2300 | Mpa |
Flexural Strength | | ISO 178 | 95 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 125 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 112 | °C |
Linear expansion coefficient | Flow | ASTM D696 | 0.000070 | cm/cm/°C |
Linear expansion coefficient | 横动 | ASTM D696 | 0.000070 | cm/cm/°C |
Tensile Strength(Break) | | ISO 527-2/5 | 50 | Mpa |
Tensile Elongation (Break) | | ISO 527-2/50 | 7 | % |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1000000000000000 | ohms |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
proportion | | ASTM D792 | 1.19 | g/cm³ |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.00 mm | UL 94 | V-1 | 无 |
Flame Rating | 1.50 mm | UL 94 | V-0 | 无 |
Flame Rating | 2.00 mm | UL 94 | 5VB | 无 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.