PC LEXAN™ XHT1141-BK1C141 SABIC INNOVATIVE US
90
- Unit Price:
- $4820 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 64MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Architectural Application Automotive External Parts Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.30 | % | |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 16.0 | cm3/10min |
| 330°C/2.16 kg | ISO 1133 | 70.0 | cm3/10min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.60 到 0.90 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO 178 | 2400 | Mpa | |
| Flexural Stress | ISO 178 | 100 | Mpa | |
| Tensile Modulus | ISO 527-2/1 | 2400 | Mpa | |
| Tensile Stress | Yield | ISO 527-2/50 | 65.0 | Mpa |
| Break | ISO 527-2/50 | 60.0 | Mpa | |
| Tensile Strain | Yield | ISO 527-2/50 | 6.5 | % |
| Break | ISO 527-2/50 | 80 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 150 | °C |
| -- | ISO 306/B120 | 152 | °C | |
| Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 144 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 132 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 125 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 290 到 335 | °C | ||
| Mold Temperature | 85 到 130 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 270 到 315 | °C | ||
| Middle Temperature | 280 到 325 | °C | ||
| Front Temperature | 290 到 335 | °C | ||
| Nozzle Temperature | 285 到 330 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 90 | rpm | ||
| Vent Depth | 0.025 到 0.080 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 | kJ/m² |
| 23°C | ISO 179/1eA | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 14 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.