Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 280°C/2.16kg | ASTMD1238 | 10 | g/10min |
Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 27 | g/10min |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 16 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ASTMD1238 | 13.0 | cm3/10min |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.050到0.10 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.20到0.40 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
--1 | | ASTMD638 | 8760 | Mpa |
fracture | | ISO527-2/50 | 2.4 | % |
fracture | | ISO527-2/50 | 120 | Mpa |
Break | | ASTMD638 | 2.4 | % |
Break | | ASTMD638 | 120 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
0.45MPa, Unannealed,3.20mm Span | | ISO75-2/Bf | 127 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 124 | °C |
0.45MPa, Unannealed,3.20mm | | ASTMD648 | 126 | °C |
Flow:-40 to 40°C | | ASTME831,ISO11359-2 | 2.1E-05 | cm/cm/°C |
Flow:-40 to 40°C | | ASTME831 | 6.9E-05 | cm/cm/°C |
Flow:-40 to 40°C | | ISO11359-2 | 7.1E-05 | cm/cm/°C |
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 122 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1.10GHz | 内部方法 | 0.014 | |
Dissipation Factor? | 1.90GHz | 内部方法 | 0.013 | |
Dissipation Factor? | 5.00GHz | 内部方法 | 0.012 | |
Dielectric Constant | 1.10GHz | 内部方法 | 3.52 | |
Dielectric Constant | 1.90GHz | 内部方法 | 3.44 | |
Dielectric Constant | 5.00GHz | 内部方法 | 3.51 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/2U | 50 | kJ/m² |
23°C | | ASTMD4812 | 700 | J/m |
23°C | | ASTMD256 | 150 | J/m |
23°C5 | | ISO180/1U | 40 | kJ/m² |
23°C4 | | ISO180/1A | 14 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.